Electrolyte separator for VBR with vanadium barrier layer

Catalog Number	ACMA00062982
Description	The perfluorinated sulfonic acid ion exchange membranes for vanadium redox battery, also called the proton exchange membranes, are produced with the new casting method, the casting process can be combined with doping technology.
Density	1.98
Application	The Perfluorinated Sulfonic Acid Ion-Exchange Membrane is used for vanadium flow batteries.
Acid Capacity	0.1 meq/g
Electrical Conductivity	0.1 S/cm
Elongation At Break	1.83
Length Increase	10% ( 23℃, from 50% RH to water soakage ) 15% ( 100℃, from 50% RH to water soaked )
Moisture Content	4% ( 23℃,relative humidity is 50% )
Size	Sheet:600mm*600mm;800mm*800mm;1000mm*1000mm Continuous Roll: 800mm width and 680mm with continuous roll
Specification	sheet/continuous roll
Tensile Strength	38 MPa ( 23℃, 50% RH, Isotropy)
Thickness	51 μm, 64 μm, 76 μm, 89 μm, 102 μm, 127 μm, 183 μm, 254 μm
Thickness Increase	10% ( 23℃, from 50% RH to water soakage ) 15% ( 100℃, from 50% RH to water soaked )
Type	Cation
Water Absorption	50±5% ( 100℃, 1h)
Weight	100 g/m2, 125 g/m2, 150 g/m2, 176 g/m2, 200 g/m2, 250 g/m2, 360 g/m2, 500 g/m2