Non-reinforced Anion Exchange Membrane,Thickness:30𝜇m,Tensile Strength 20-40 MPa

Catalog Number	ACMA00062913
Description	This is a non-reinforced Anion Exchange Membrane (AEM) with very low resistance, high selectivity and high stability in pH acidic and basic environments. The polymer backbone for this membrane is based on a proprietary hydrocarbon resin.
Density	3.5 - 4.4 mg·cm-2
Application	Electrodialysis for demineralization, desalination, capacitive deionization and others. This membrane can also be used for standard alkaline fuel cell and electrolysis applications that are utilizing slightly alkaline solutions (1-2 Molar).
Storage	Dry Form: The membrane can be stored dry for an unlimited amount of time. However, the membrane has to be conditioned (washed and rinsed) prior to use. Wet Form: Storage for short and medium time scale (hours up to several weeks) may be done in unsealed containers in 0.5 - 1.5 wt% NaCl solution or comparable neutral pH electrolytes.
Backing Foil	PET Foil
Bubble Point	> 2.5 bar (Test in Water)
Color Form	Transparent / Brown
Delivery Form	Dry
Dimensional Swelling	0 - 2 %
Electrical Conductivity	3.0 - 7.0 (in Cl- form) mS·cm-1
Elongation At Break	30 - 60 %
Ionic Form	Bromide (Br-)
Non-Std Modulus	1200 - 1700 MPa
Notice For Use	The membrane is delivered in bromide form and dry form. Depending on application and cell design, assembling is possible in dry form (without pretreatment) or wet form. For optimum performance it is recommended to rinse the membrane in NaCl solution (e.g. 0.5 M NaCl solution at 25°C for 24 hrs) to remove any additive from the membrane. Place the membrane sample between stabilizing meshes / spacers in order to avoid curling. Do not let the membrane dry out since micro-cracks may likely occur during shrinkage.
pH	0 -14 at 25°C
Reinforcement	None
Selectivity	92 - 96 %
Sheet Resistance	0.3 - 0.6 (in Cl- form) Ω·cm2
Size	10 x 10 cm, 20 x 30 cm
Tensile Strength	20 - 40 MPa
Thickness	30 micrometers (1.19 mil)
Total Exchange Capacity	1.6 - 2.0 meq/g
Type	Anion
Water Absorption	15 - 30 wt % (in H2O at 34°C)
Yield Strength	25 - 40 MPa at 23°C / 64 % R.H.