Non-reinforced Cation Exchange Membrane,Thickness:50𝜇m,TotalExchangeCapacity:1.4-1.5 meq/g

Catalog NumberACMA00062955

CategoryCation Exchange Membranes

Description	This product is a non-reinforced Cation Exchange Membrane (CEM) with very low resistance, high selectivity and high stability in pH acidic and basic environments.
Density	7.5 - 8.5 mg·cm-2
Application	Designed for Electrodialysis for demineralisation, desalination, capacitive deionization and others.
Storage	Dry form: Membranes can be stored dry for an unlimited period of time. However, the membrane must be conditioned (washed and rinsed) before use. Wet form: Available for short- and medium-term storage (hours to weeks) in unsealed containers in 0.5 - 1.5 wt% NaCl solution or similar neutral pH electrolyte.
Backing Foil	PET Foil
Bubble Point	> 2.5 bar (Test in Water)
Color Form	Transparent / Brown
Delivery Form	Dry (non-activated)
Dimensional Swelling	0 - 2 %
Electrical Conductivity	2.5 - 3.5 (in Na+ form) mS·cm-1
Elongation At Break	50 - 250 %
Hydroxyl Transfer Rate	200 - 500 µmol·min-1·cm-2
Ionic Form	H-form
Non-Std Modulus	1500 - 2500 MPa
Notice For Use	Membranes are delivered in H and dry versions. Depending on the application and cell design, assembly can be done in dry (without pretreatment) or wet form. For optimal performance, it is recommended to rinse the membrane in a NaCl solution (e.g., 0.5 M NaCl solution at 25°C for 24 hours) to remove any additives on the membrane. Place the membrane sample between stabilizing mesh/spacers to avoid curling. Do not let the film dry as micro-cracks may appear during shrinkage.
Reinforcement	None
Selectivity	97 - 99 %
Sheet Resistance	1.5 - 2.3 (in Na+ form) Ω·cm2
Size	10 x 10 cm, 20 x 30 cm
Tensile Strength	50 - 80 MPa
Thickness	50 micrometers (1.97 mil)
Total Exchange Capacity	1.4 - 1.5 (in Na+ form) meq/g
Type	Cation
Water Absorption	15 - 35 wt % (in H2O at 25°C)
Yield Strength	40 - 60 MPa at 23°C / 54 % R.H.