PK-reinforced Anion Exchange Membrane,Thickness:130𝜇m,TotalExchangeCapacity:0.7-1.0 meq/g

Catalog Number	ACMA00062928
Description	This is a PK-reinforced Anion Exchange Membrane (AEM) with high proton blocking capability, high selectivity, very high mechanical stability, and high stability in acidic and caustic environment.
Density	10 - 13 mg·cm-2
Application	This is designed for the processing of concentrating acidic solutions, electrodialysis and electrodialysis with bipolar membranes.
Storage	Dry Form: The membrane can be stored dry for an unlimited amount of time. However, the membrane has to be conditioned (washed and rinsed) prior to use. Wet Form: Storage for short and medium time scale (hours up to several weeks) may be done in unsealed containers in 0.5 - 1.5 wt% NaCl solution or comparable neutral pH electrolytes.
Backing Foil	None
Bubble Point	> 3 bar (Test in Water)
Color Form	Brown
Delivery Form	Dry
Dimensional Swelling	0 - 1 %
Electrical Conductivity	1.0 - 2.5 in Cl- form and 10 - 20 in SO42- form mS·cm-1
Elongation At Break	15 - 40 %
Ionic Form	Bromide (Br-)
Non-Std Modulus	1000 - 1800 MPa
Notice For Use	The membrane is delivered in the bromide form and dry. Depending on application and cell design, assembling is possible in dry form (without pretreatment) or wet form. For optimum performance it is recommended to rinse the membrane in NaCl solution (e.g. 0.5 M NaCl solution at 25°C for 24 hrs) to remove any additive from the membrane. Place the membrane sample between stabilizing meshes / spacers in order to avoid curling. Do not let the membrane dry out since micro-cracks may likely occur during shrinkage.
pH	0 -14 at 25°C
Reinforcement	PK
Selectivity	93 - 98 %
Sheet Resistance	5.0 - 9.0 in Cl- form and 10 - 20 in SO42- form Ω·cm2
Size	10 x 10 cm, 20 x 30 cm
Tensile Strength	40 - 80 MPa
Thickness	130 micrometers (5.1 mil)
Total Exchange Capacity	0.7 - 1.0 (in Cl- form) meq/g
Type	Anion
Water Absorption	5 - 15 wt % (in H2O at 33°C)
Yield Strength	20 - 30 MPa at 23°C / 63 % R.H.